High Speed Steel (HSS) M2 Solid Scrap Supplier, Stockist in Mumbai, India
IMI Alloys India LLP is a leading manufacturer, supplier, and dealer of HSS M2 Solid Scrap. We provide this high-quality Solid Scrap to all sorts of applications. The range is available in custom manufacture as per the requirements of the clients. We manufacture our items using excellent grades and raw materials. Our highly skilled professionals design this Solid Scrap as per national and international standards. HSS M2 grade contains high carbon. M2 is a high-speed steel grade. This chemical composition is well suitable for various applications. This alloy shows physical properties like density, specific gravity, modulus of elasticity, and machinability. Our HHS M2 Solid Scarp shows thermal expansion. Our HSS M2 Solid Scarp has resistance to wear. This alloy offers hardness.
HSS M2 Solid Scarp is used in various cutting tools where demands for hot hardness are high, such as twist drills, reamers, broaching tools, milling tools, taps, and metal saws. HSS M2 solid scrap is also suitable for cold work applications such as punching, forming, and pressing tools. This material goes through a physical vapour deposition process to increase the performance and this tools life span.
Table of Content
- What is High Speed Steel (HSS) M2 Solid Scrap
- Standard Specification For High Speed Steel M2 Solid Scrap
- High Speed Steel M2 Solid Scrap Equivalent Grades
- Chemical Composition of M2 High Speed Steel Solid Scrap
- Mechanical Properties of High Speed Steel M2 Solid Scrap
- Searches Related to High Speed Steel M2 Solid Scrap
- High Speed Steel (HSS) M2 Solid Scrap Applications
- Export Destinations for High Speed Steel M2 Solid Scrap
HSS M2 Solid Scrap, M2 HSS Solid Scrap, Tool Steel Solid Scrap, High Speed Steel M2 Solid Scrap Exporter, HSS M2 Solid Scrap Stockholder, M2 Solid Scrap, M2 High Speed Steel Solid Scrap, DIN HS6-5-2 Solid Scrap, GB W6Mo5Cr4V2 High Speed Steel Solid Scrap, UNS T11302 HSS Solid Scrap, High Speed Steel 1.3343 Solid Scrap, SKH9 High Speed Steel Solid Scrap, High Speed Steel M2 Scraps Supplier in Mumbai, India.
Our HSS M2 Solid Scarp mechanical properties have mechanical properties like compressive yield strength, abrasion, Poisson’s ratio, and elastic modulus. Using the grinding method, we are shaping this alloy, so this alloy is easily machinable. Our company provides this product has high demand in various applications due to their property and relative economy. Our product is mainly used for all metal-cutting tools for roughing or finishing. It is mostly suitable for cold-forming tools such as cold extrusion rams and dies and cutting and precision cutting tools, plastic moulds with elevated wear resistance and screws. Whether you’re interested in HSS M2 solid scrap or HSS M42 solid scrap, we’ve got you covered. Our comprehensive range also includes general HSS solid scrap. Explore our collection to find the perfect HSS scrap for your needs: HSS M2 Solid Scrap, HSS M42 Solid Scrap, and HSS Solid Scrap.
High Speed Steel M2 Solid Scrap Dealer, HSS M2 Solid Scraps Stockist, HSS Scrap Manufacturer, High Speed Steel(HSS)-M2 Solid Scrap, Buy Comprehensive Variety of High Speed Tool Steel M2 Solid Scrap, M2 HSS Tool Steel Solid Scrap, High Speed Steel M2 Industrial Solid Scrap, High Speed Steel T11302 Solid Scrap, M2 HSS Black Solid Scrap Stockist in India.
Specifications of High Speed Steel M2 Solid Scrap
- Grade: M2
- Material: High Speed Steel
- Scrap Form: Solid HSS M2 grade Scrap
- Scrap Form: Mixed
- Application : Lathe Tools, Milling Cutter, Cutter Blades, Boring Tools, Twist drills, Milling Knives, Reamers, Taps, Metalcutting saws, Screw Cutting Tools, File Cutter’s Chissels, Drills, Hobs, Drill Bits, Tread cutting tools etc
Equivalent Grades of High Speed Steel M2 Solid Scrap
| Country | USA | German | Japan |
| Standard | – | DIN EN ISO 4957 | JIS G4403 |
| Grades | M2 | 1.3343 | SKH51 |
Chemical Composition of M2 High Speed Steel Solid Scrap
| ASTM – | C | Mn | P | S | Si | Cr | V | Mo | W | |||||||
| M2 regular C | 0.78 | 0.88 | 0.15 | 0.40 | 0.03 | 0.03 | 0.20 | 0.45 | 3.75 | 4.50 | 1.75 | 2.20 | 4.50 | 5.50 | 5.50 | 6.75 |
| DIN ISO 4957 | C | Mn | P | S | Si | Cr | V | Mo | W | |||||||
| 1.3343 | 0.86 | 0.94 | … | … | … | … | … | 0.45 | 3.80 | 4.50 | 1.70 | 2.10 | 4.70 | 5.20 | 5.90 | 6.70 |
| JIS G4403 | C | Mn | P | S | Si | Cr | V | Mo | W | |||||||
| SKH51 | 0.80 | 0.88 | … | 0.40 | 0.03 | 0.03 | … | 0.45 | 3.80 | 4.50 | 1.70 | 2.10 | 4.70 | 5.20 | 5.90 | 6.70 |
Mechanical Properties of High Speed Steel M2 Solid Scrap
| Density | 0.294 lb/in3 (8138 kg/m3) |
| Specific Gravity | 8.15 |
| Modulus of Elasticity | 0.294 lb/in3 (8138 kg/m3) |
| Thermal conductivity | 24 Btu/ft/hr/°F 41.5 W/m/°K |
| Machinability | 65% of a 1% carbon steel |
| Mechanical properties | Metric | Imperial |
| Hardness, Rockwell C (tempered at 1150°F, quenched at 2200°F) | 62 | 62 |
| Hardness, Rockwell C (as hardened, quenched at 2200°F) | 65 | 65 |
| Compressive yield strength (when tempered at 300°F) | 3250 MPa | 471000 psi |
| Izod impact unnotched (when tempered at 300°F) | 67 J | 49.4 ft-lb |
| Abrasion (loss in mm3, as-hardened; ASTM G65) | 25.8 | 25.8 |
| Abrasion (loss in mm3, tempered at 1275°F; ASTM G65) | 77.7 | 77.7 |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elastic modulus | 190-210 GPa | 27557-30458 ksi |
Thermal Properties of High Speed Steel M2 Solid Scrap
| Thermal properties | Metric | Imperial |
| CTE, linear (@20.0 – 100°C/ 68.0 – 212°F) | 10 μm/m°C | 5.56 μin/in°F |
| CTE, linear (@20.0 – 500°C/68.0 – 932°F) | 12.2 μm/m°C | 6.78 μin/in°F |
| CTE, linear (@20.0 – 850°C/68.0 – 1560°F) | 12.6 μm/m°C | 7 μin/in°F |
Searches Related to High Speed Steel M2 Solid Scrap
Applications For High Speed Steel M2 Solid Scrap
Generally, high speed steels are used for machining at high speeds. HSS M2 steel materials are widely used for:
- Broaches
- Drills
- Hobs
- Knurling Tools
- Lathe Tools
- Milling Cutters
- Nut Piercers
- Planer Tools
- Reamers
- Shaving Tools
- Taps
- Thread Cutting Tools